Influence of Р6m5 Steel Structure on Modes of Low Temperature Nitrocementation

Begatov Jahongir Mukhammadjonovich; Platoshina Malika Mirkamal kizi

Begatov Jahongir Mukhammadjonovich PhD, Associate Professor Joint Belarusian-Uzbek Interdisciplinary Institutem Applied Technical Qualifications, Tashkent, Uzbekistan
Platoshina Malika Mirkamal kizi Senior Lecturer at the Department of Energy and Applied Sciences, Tashkent Kimyo International University, Tashkent, Uzbekistan

Keywords: wear resistance, tool, high-speed steel, hardening, hardness

Abstract

The article discusses a method of hardening tools made of high-speed steel grade P6M6 in order to obtain higher wear resistance. Research has been carried out on the effect of final tempering temperature on the hardness of steel, and research has also been carried out to determine the optimal temperature of nitrocarburization, in order to obtain high hardness values with a general reduction in tool processing time. To determine the effect of tempering temperature on the hardness of Р6M5 steel, samples were prepared that were quenched from standard temperatures of 1200-1230°C and subjected to tempering from different temperatures. Studies have shown that the highest hardness values are achieved when tempering 540-560°С, and with a further increase in tempering temperature, up to a temperature of 620°С, there is no critical decrease in steel hardness. This circumstance makes it possible to carry out a single final tempering at a temperature of 600-620°С.

References

1. Struk V.A. and others. Materials science in mechanical engineering and industrial technologies. M.: Publishing house "Intellect", 2010. –536 p.
2. Fitosov G.P. Materials science and metal technology. – M.: Higher School, 2006. – 861 p.
3. Chudni O.V., Gladova G.V. Selection of materials and methods for strengthening parts of transport mechanical engineering, M.: MADI. 2015. – 118 p.
4. Arzamasov B.N. Materials Science: Textbook for Universities - M.: MSTU named after Bauman, 2008 – 648 p.
5. Babul T.D., Kucharieva T.G. The influence of the initial structure and tool steels on the thickness and hardness of layers obtained as a result of carbonitriding MiTOM, 2004. No. 7 - P. 17-20
6. Bektemirov, B.Sh., Saydakhmedov, R.Kh. Thermal properties of thermal barrier coatings (TBC). Lityo i metallurgiya 2018: sbornik nauchnih rabot IV Mejdunarodnoy nauchno-prakticheskoy internet konferenciy studentov i magistrantov. Minsk: BNTU, 2018. Pp. 48-49.
7. Risbekov, S.S., Bektemirov, B.Sh. Zirconia toughened alumina (zta). Lityo i metallurgiya 2019: sbornik nauchnih rabot IV Mejdunarodnoy nauchno-prakticheskoy internet konferenciy studentov i magistrantov. Minsk: BNTU, 2019. Pp. 85-86.
8. Alikulov, А. K., Bektemirov, B. Sh., Norkhudjaev, F. R., & Mirzarakhimova, Z. B. (2023). Determination of Density of the Samples Made of Copper Based Materials. Best Journal of Innovation in Science, Research and Development, 2(9), 106-111.
9. А. Kh. Alikulov, U.N. Ruziev, F. Mengaliyev “Аnalysis of materials for contact spot welding electrodes”. “International Journal of Discoveries and Innovations in Applied Sciences (IJDIAS) ISSN 2792-3983” India. 2022 (12), Р.13–16.
10. Mukhammadjonovich, B. J. (2023). Technological Features of the Processes of Simultaneous Saturation of Steel with Nitrogen and Carbon. Nexus: Journal of Advances Studies of Engineering Science, 2(5), 42-46.
11. Mukhammadjonovich, Begatov Jakhongir, Ergashev Meirzhan Sattarugli, and Platoshina Malika Mirkamalkizi. "EFFECT OF QUENCHING AND TEMPERING TEMPERATURES ON THE STRUCTURE FORMATION OF 4XMFC, 4X5MF1C STEELS DURING LOW-TEMPERATURE NITRO-CEMENTATION." International Journal of Mechatronics and Applied Mechanics 13 (2023): 230-235.
12. Jakhongir Begatov, Sobirov Bekzodbek Ahmadjonovich, Makhmuda Yakubova, Dilnoza Kuchkarova, Malika Djalilova. the properties of high-speed steel р6м5, depending on the combined chemical heat treatment. International Journal of Mechatronics and Applied Mechanics, Issue 11, Pp: 119- 122, 2022.